EAA 5990物性表物理性能測試條件測試方法測試結(jié)果單位熔體質(zhì)量流動速率125°C/2.16kg2ASTMD1238,ISO113365g/10min190°C/2.16kg3ASTMD1238,ISO11331300g/10min共聚單體含量4內(nèi)部方法20.0%機械性能測試條件測試方法測試結(jié)果單位拉伸模量-2%正割模壓成型ASTMD638,ISO527-222.1Mpa抗張強度斷裂,模壓成型ASTMD638,ISO527-26.21Mpa伸長率斷裂,模壓成型ASTMD638,ISO527-2350%拉伸模量-2% SecantCompression MoldedMPaASTM D-63822.1Compression MoldedMPaISO 527-222.1拉伸斷裂強度Compression MoldedMPaASTM D-6386.21Compression MoldedMPaISO 527-26.21拉伸斷裂伸長率Compression Molded%ASTM D-638350Compression Molded%ISO 527-2350熱性能測試條件測試方法測試結(jié)果單位維卡軟化點℃ASTM D-1525℃ISO 306熔融溫度℃Internal Method75維卡軟化溫度ASTMD1525,ISO30640.0°C溶融溫度（DSC）內(nèi)部方法75.0°C基本性能測試條件測試方法測試結(jié)果單位熔融指數(shù)125℃/2.16kgg/10minASTM D-1238125℃/2.16kgg/10minISO 1133190℃/2.16kgg/10minASTM D-℃/2.16kgg/10minISO 11331300單體含量%Internal Method