熱性能額定值單位測試方法熱變形溫度 (0.45 MPa, 未退火)115℃ASTM D648    (0.45 MPa, 未退火)85.0℃ISO 75-2/B    (1.8 MPa, 未退火)51.0℃ASTM D648    (1.8 MPa, 未退火)45.0℃ISO 75-2/B脆化溫度< -100℃ISO 974玻璃轉(zhuǎn)化溫度0.00℃ISO 11357-2熔融溫度211℃ISO 11357-3, ASTM D3418線形膨脹系數(shù) (流動: -40 到 23℃)0.00015cm/cm/℃ASTM E831, ISO 11359-2    (流動: 23 到 55℃)0.00018cm/cm/℃ASTM E831, ISO 11359-2    (流動: 55 到 120℃)0.00018cm/cm/℃ASTM E831, ISO 11359-2    (橫向: -40 到 23℃)0.00015cm/cm/℃ASTM E831, ISO 11359-2    (橫向: 23 到 55℃)0.00018cm/cm/℃ASTM E831, ISO 11359-2    (橫向: 55 到 120℃)0.00018cm/cm/℃ASTM E831, ISO 11359-2其它額定值單位測試方法干燥溫度100℃干燥時間2.0 到 3.0hr建議的 水分含量< 0.080%Melt Temperature, Optimum (Injection Molding)240℃模具溫度45.0 到 55.0℃Mold Temperature, Optimum (Injection Molding)45℃